Stacker Travelling Wheel Alloy Steel Castings Mill Liners EN 100831-1991

Browse Categories

Wuxi Orient Anti-wear Engineering Co.,Ltd.

City: wuxi

Province/State:jiangsu

Tel:86--17768338719

Contact Person:
3Vivian Xu
View Contact Details

Stacker Travelling Wheel Alloy Steel Castings Mill Liners EN 100831-1991

Brand Name Chen's Liner
Model Number DF712
Certification ISO 9001:2008
Place of Origin Jiangsu, China (Mainland)
Minimum Order Quantity 4 Ton/Tons
Price Discuss in email
Payment Terms L/C,T/T
Supply Ability 4500 Ton/Tons per Year
Delivery Time It depends on the quantity to be ordered.
Packaging Details Packed by steel pallets.
Port Shanghai
Material High Cr White Iron
Hardness More than HRC40
Impact Value More than AK78J
Yield strength ≥930(95)σs (MPa)
Elongation ≥12%
Dimensions As per drawings
Product Name Mill Liners
Application: Coal mill, Mine mill, Cement mill
OEM: Yes
MOQ: 2 Tons
Detailed Product Description

Stacker Travelling Wheel Alloy Steel Castings Reliable EN 100831-1991
 

 
 
1. Yield strength: σs (MPa):≥930(95);
2. Strength of extension σb (MPa):≥1080(110);
3. Percentage reduction of area ψ (%):≥45;
4. Elongation: δ5 (%):≥12;
5. Impact Value: more than AK78J.


 
 
The general advantages in ball mills are as follows: 
 

Output Increased

5~20%

Power Consumption Reduced  

5~20%

Maintenance Decreased 

Above 98%

The liners are easily installed and existing mills need no modification.

 
The additional advantages in cement mills are as follows:

 

No leakage of slurry

No repairs during service periods

Better reliability and stability

Production Improvement

Noise reduction

 
 
Technical Parameters

 

ItemCr-Mo 
Alloy Steel I
Cr-Mo 
Alloy Steel II
Cr-Mo 
Alloy Steel III
C0.30-0.500.65-0.900.40-0.90
Si0.50-1.20≤0.750.70-1.20
Mn0.40-1.200.50-1.200.60-1.00
Cr1.70-2.501.50-2.504.00-7.00
S≤0.04≤0.06≤0.04
P≤0.04≤0.06≤0.06
Mo≤0.5≤0.5≤0.5
Cu0.10-0.60≤0.250.20-0.40
Ni≤0.50≤0.30≤0.30
Re≤0.02≤0.02≤0.02
Equivalent
Specifications
DL/T 681-1999
GB/T26651-2011
AS 2074 L2B
Mod
DL/T681-1999
Material TypeMartensite SteelMartensite or
Pearlitic Cr Mo Steel
Martensite Steel
HardnessHRc≥48HB470&
HB321-370
HRc≥50
Impact ValueAK≥40J-AK≥10J

 

ItemHigh Cr white ironHigh Cr Alloy SteelHigh Manganese SteelNi-Hard cast iron
C2.40-3.201.1-2.20.90-1.302.40-3.60
Si0.60-1.200.60-1.20≤0.08≤0.08
Mn0.50-1.000.50-1.0011.00-18.00≤2.0
Cr12.00-30.0011.00-30.001.50-2.201.5-10.0
S≤0.04≤0.04≤0.04≤0.15
P≤0.06≤0.06≤0.06≤0.15
Mo0.10-0.300.10-0.30≤1.0≤0.10
Cu0.10-1.000.10-1.00--
Ni0-0.300-0.30-3.3-10.0
Re----
Equivalent
Specifications
GB/T 8263-1999
AS 2027 Cr27
AS 2027 CrMo15/3
AS 2027 CrMo20/2/1
ASTM A532 Class III type A25%Cr
ASTM A532 Class II type B15%Cr-Mo
BS 4844 3E
DIN1695
NFA32401
BG/T 5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A 128
DIN GX120Mn12
AFNOR:Z120Mn12
GB/T 8263-1999
AS 2027/Ni-Cr1-550
AS 2027/Ni-Cr2-500
AS 2027/Ni-Cr4-500
AS 2027/Ni-Cr4-600
AS 2027/Ni-Cr4-630
ASTM A 532 1-A,B,C,D
ASTM A 532 2-A,B,C,D,E
ASTM A 532 3-A
Material TypeMartensite matrixAustenitic Mn Steel-
HardnessHRc≥56HB≤300HRc≥56
Impact ValueAK≥4JAK≥80J-

 

Our foundry has complete melting,heat treatment and test equipments,such as mid-frequency induction electrical 
furnaces,quenching and tempering furnaces,blast shot,spectrometer,Rockwell and Brinell Hardness tester,impactor.   
UT tester and metallographic microscope.We achieved the certificate of quality management 

system ISO 9001:2000.We have been exporting castings to oversea markets,such as Brazil,

Australia and South Africa.

 